Electron blocking layers for electronic devices

ABSTRACT

Methods and apparatuses for electronic devices such as non-volatile memory devices are described. The memory devices include a multi-layer control dielectric, such as a double or triple layer. The multi-layer control dielectric includes a combination of high-k dielectric materials such as aluminum oxide, hafnium oxide, and/or hybrid films of hafnium aluminum oxide. The multi-layer control dielectric provides enhanced characteristics, including increased charge retention, enhanced memory program/erase window, improved reliability and stability, with feasibility for single or multi state (e.g., two, three or four bit) operation.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present patent document is a continuation-in-part of PCTInternational Patent Application No. PCT/US2007/087167, which was filedon Dec. 12, 2007, and which claims priority to U.S. Provisional PatentApplication Ser. No. 60/931,488, which was filed on May 23, 2007, and toU.S. patent application Ser. No. 11/743,085, filed on May 1, 2007, whichis a continuation-in-part of U.S. patent application Ser. No.11/688,087, filed on Mar. 19, 2007, which is a continuation-in-part ofU.S. patent application Ser. No. 11/641,956, filed on Dec. 20, 2006, theentire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

The present disclosure relates to memory devices, and more particularly,to flash memory devices.

BACKGROUND OF THE INVENTION

Non-volatile memory devices, such as flash memory devices, are memorydevices that can store information even when not powered. A flash memorydevice stores information in a charge storage layer that is separatedfrom a “control gate.” A voltage is applied to the control gate toprogram and erase the memory device by causing electrons to be storedin, and discharged from the charge storage layer.

A control dielectric is used to isolate the control gate from the chargestorage layer. It is desirable for the control dielectric to blockcharge flow between the charge storage layer and control gate. High-kdielectric layers can serve as efficient charge-blocking layers. Theyhave been used as the control dielectric layer for flash memory devices,such as Samsung's TANOS devices, to enable the down-scaling of flashmemory devices below 40 nm. The control dielectric layer may be a singlelayer of Al₂O₃, typically with a thickness of less than 20 nm. However,Al₂O₃ does not completely block charge transport and leads to programand erase saturation at lower voltage windows.

What is needed are improved, longer lasting non-volatile memory devices,with improved charge blocking characteristics. Furthermore, multi-statememory devices exist, which can store more than one bit of informationper memory cell. What is needed are improved multi-state memory devicesthat can store multiple bits per cell with relatively largeprogram/erase voltage windows of operation.

BRIEF SUMMARY OF THE INVENTION

Described herein are non-volatile memory devices and a method of makinga memory device that may provide advantages over existing devices andmethods.

According to one embodiment, a gate stack of a memory device includes acharge storage layer between a tunneling dielectric layer and a controldielectric layer, and a dielectric layer (e.g., a charge blocking layer)including a dielectric material is adjacent to the control dielectriclayer. An amount of at least a first component of the dielectricmaterial varies in a predetermined manner across a thickness of thedielectric layer.

According to another embodiment, a gate stack of a memory deviceincludes a charge storage layer between a tunneling dielectric layer anda control dielectric layer having a thickness of about 5 nm or less, anda charge blocking layer comprising a dielectric material is adjacent tothe control dielectric layer.

According to another embodiment, a gate stack of a memory devicecomprises a charge storage layer between a tunneling dielectric layerand a control dielectric layer, and a charge blocking layer comprising adielectric material is adjacent to the control dielectric layer. Athickness of the control dielectric layer is no more than about 200% ofa thickness of the charge blocking layer.

According to another embodiment, a gate stack of a memory devicecomprises a charge storage layer between a tunneling dielectric layerand a control dielectric layer, the control dielectric layer comprisingSiO₂, and a first high-k dielectric layer comprising a first high-kdielectric material adjacent to the control dielectric layer.

According to another embodiment, a gate stack of a memory devicecomprises a tunneling dielectric layer, a charge storage layer abovesaid tunneling dielectric layer, a first dielectric layer adjacent thecharge storage layer comprising a first dielectric material having afirst dielectric constant, a second dielectric layer adjacent the firstdielectric layer comprising a second dielectric material having a seconddielectric constant, and a third dielectric layer adjacent the seconddielectric layer comprising a third dielectric material having a thirddielectric constant, wherein the first and third dielectric constantsare greater than the second dielectric constant.

According to another embodiment, the gate stack of the memory deviceincludes a charge storage layer comprising localized charge traps on atunneling dielectric layer, a first dielectric layer comprising a firstoxynitride having a first dielectric constant on the charge storagelayer, a second dielectric layer comprising an oxide having a seconddielectric constant on the first dielectric layer, and a thirddielectric layer comprising a second oxynitride having a thirddielectric constant on the second dielectric layer, where the first andthird dielectric constants are greater than the second dielectricconstant.

According to another embodiment, the gate stack of the memory devicecomprises a charge storage layer comprising a nitride on a tunnelingdielectric layer, a first dielectric layer comprising an oxide on thecharge storage layer, and a second dielectric layer comprising anoxynitride on the first dielectric layer, where the memory deviceexhibits a charge retention of 85% or greater over a period of 24 hoursat a temperature of 250° C.

According to another embodiment, a gate stack of a memory devicecomprises a charge storage layer comprising polysilicon on a tunnelingdielectric layer, a first dielectric layer comprising a first oxynitridehaving a first dielectric constant on the charge storage layer, a seconddielectric layer comprising an oxide having a second dielectric constanton the first dielectric layer, and a third dielectric layer comprising asecond oxynitride having a third dielectric constant on the seconddielectric layer, where the first and third dielectric constants aregreater than the second dielectric constant, and where the memory deviceexhibits a charge retention of 85% or greater over a period of 24 hoursat a temperature of 250° C.

According to one embodiment, a memory device includes a substratecomprising a source region, a drain region, and a channel region betweenthe source region and the drain region, and a gate stack on thesubstrate adjacent to a control gate. The gate stack includes a firstdielectric layer adjacent to the control gate, a charge storage layerbetween the first dielectric layer and a second dielectric layer, and acharge blocking layer comprising a dielectric material adjacent to thefirst dielectric layer. An amount of at least a first component of thedielectric material varies in a predetermined manner across a thicknessof the charge blocking layer.

According to one embodiment, a method of making a gate stack for amemory device includes forming a charge storage layer on a tunnelingdielectric layer, forming a control dielectric layer on the chargestorage layer, forming a charge blocking layer comprising a dielectricmaterial on the control dielectric layer and varying an amount of atleast a first component of the dielectric material across a thickness ofthe charge blocking layer.

According to another embodiment, a method of making a gate stack of amemory device includes forming a tunneling dielectric layer over asubstrate, forming a charge storage layer comprising localized chargetraps over the tunneling dielectric layer, forming a first dielectriclayer comprising a first oxide over the charge storage layer, forming asecond dielectric layer comprising a second oxide over the firstdielectric layer, forming a third dielectric layer comprising a thirdoxide over the second dielectric layer, and forming an oxynitride fromat least one of the first oxide and the third oxide, where forming theoxynitride comprises annealing at least one of the first oxide and thethird oxide in ammonia at a temperature of about 900° C. or lower,according to one embodiment, and where forming the oxynitride comprisesexposing at least one of the first oxide and the third oxide to anitrogen plasma, according to another embodiment.

BRIEF DESCRIPTION OF THE DRAWINGS/FIGURES

FIG. 1 shows a cross-sectional view of a memory device;

FIGS. 2-3 show cross-sectional views of a gate stack of a memory deviceaccording to two embodiments;

FIGS. 4A-4C are schematics showing the energy barrier to electrontunneling posed by dielectric layers according to several embodiments;

FIGS. 5-6 show cross-sectional views of a gate stack of a memory deviceaccording to other embodiments;

FIG. 7 shows a contiguous charge storage layer according to oneembodiment;

FIG. 8 shows a non-contiguous charge storage layer according to anotherembodiment;

FIGS. 9A and 9B show simulation plots related to a combination controldielectric layer, according to various embodiments;

FIGS. 10A-10C and 11A-11D show plots related to a program/erase windowfor various gate stacks having one or more charge blocking layers,according to various embodiments;

FIGS. 11E and 11F show plots related to charge retention for memorydevices including various exemplary gates stacks;

FIG. 12 shows a cross-sectional view of a gate stack of a memory deviceaccording to another embodiment;

FIG. 13 shows a plot of erase time (x-axis) versus flat-band voltage(y-axis) for gate stacks using a nitride layer as the charge trappinglayer, comparing a gate stack without one or more charge blocking layersand an improved gate stack with a charge blocking layer;

FIG. 14 shows a plot of the number of program and erase cycles (x-axis)versus the flat-band voltage (y-axis) using the improved gate stack ofFIG. 13; and

FIG. 15 shows a chart of room temperature charge retention mapping time(x-axis) versus flat-band voltage (y-axis) using the improved gate stackof FIG. 13.

FIG. 16A-16B show simulation plots related to a combination controldielectric layer, according to several embodiments;

FIGS. 17A-17C show simulation plots related to a charge blocking layerhaving a composition gradient, according to several embodiments;

FIG. 18 shows a simulation plot related to a charge blocking layerhaving a composition gradient, according to several embodiments;

FIGS. 19A-19D show simulation plots related to a charge blocking layerhaving a composition gradient, according to several embodiments;

FIG. 20 shows a flowchart of a method for forming an electronic device,such as a memory device, according to one embodiment.

In the drawings, like reference numbers indicate identical orfunctionally similar elements. Additionally, the left-most digit(s) of areference number generally identifies the drawing in which the referencenumber first appears.

DETAILED DESCRIPTION OF THE INVENTION Introduction

It should be appreciated that the particular implementations shown anddescribed herein are exemplary and are not intended to otherwise limitthe scope of the present invention in any way. Indeed, for the sake ofbrevity, conventional electronics, manufacturing, semiconductor devices,and other functional aspects of the systems (and components of theindividual operating components of the systems) may not be described indetail herein.

It should be understood that the spatial descriptions (e.g., “above,”“below,” “up,” “down,” “top,” “bottom,” etc.) made herein are forpurposes of illustration only, and that devices described herein can bespatially arranged in any orientation or manner.

The terms “adjacent,” “on,” “over,” and “overlying,” as used herein todescribe the relationship of one layer to another layer, are intended tobe interpreted broadly to include layers in direct contact with oneanother and layers spaced apart by one or more intervening layers.Similarly, the term “between” is intended to be interpreted broadly toinclude a layer that is directly between two other layers or spacedapart from two other layers but still intermediate the two other layers.

Memory Device Embodiments

Embodiments of the present invention are provided in the followingsub-sections for electronic devices, such as non-volatile memorydevices, including flash memory devices. Furthermore, embodiments forenhanced memory devices, such as multistate memory devices, aredescribed. These embodiments are provided for illustrative purposes, andare not limiting. The embodiments described herein may be combined inany manner. Additional operational and structural embodiments will beapparent to persons skilled in the relevant art(s) from the descriptionherein. These additional embodiments are within the scope and spirit ofthe present invention.

A conventional charge storage layer memory cell or structure isprogrammed by applying appropriate voltages to the source, drain, andcontrol gate nodes of the memory structure for an appropriate timeperiod. Electrons are thereby caused to tunnel or be injected (e.g., viachannel hot electrons) from a channel region to a charge storage layer,which is thereby “charged.” The charge stored in the charge storagelayer sets the memory transistor to a logical “1” or “0.” Depending onwhether the memory structure includes an enhancement or depletiontransistor structure, when the charge storage layer is positivelycharged or contains electrons (negative charge), the memory cell will orwill not conduct during a read operation. When the charge storage layeris neutral (or positively charged) or has an absence of negative charge,the memory cell will conduct during a read operation by a proper choiceof the gate voltage. The conducting or non-conducting state is output asthe appropriate logical level. “Erasing” is the process of transferringelectrons from the charge storage layer (or holes to the charge storagelayer) (i.e., charge trapping layer). “Programming” is the process oftransferring electrons onto the charge storage layer.

The enhancement of performance and charge retention properties ofnonvolatile memory devices using metal or semiconductor nanocrystals(such as colloidal quantum dots or quantum dots formed using processessuch as chemical vapor deposition or physical vapor deposition) ornonconductive nitride based charge trapping layers embedded in a high-kdielectric matrix, may be important to overcome the scaling limitationsof conventional non-volatile memories beyond the 50 nm technology nodeand to fully enable reliable multi-bit operation.

FIG. 1 shows a detailed cross-sectional view of a memory device 100,according to an exemplary embodiment. As shown in FIG. 1, memory device100 is formed on a substrate 102. Memory device 100 includes sourceregion 112, channel region 114, drain region 116, a control gate or gatecontact 118, a gate stack 120, a source contact 104, a drain contact106. Source region 112, channel region 114, and drain region 116 areconfigured generally similar to a transistor configuration. Gate stack120 is formed on channel region 114. Gate contact 118, which mayalternatively be referred to as a control gate or gate electrode, isformed on gate stack 120.

Memory device 100 generally operates as described above for conventionalmemories having charge storage layers. However, charge storage layermemory device 100 includes gate stack 120. Gate stack 120 provides acharge storage layer for memory device 100, and further features, asfurther described below. When memory device 100 is programmed, electronsare transferred to, and stored by, the charge storage layer of gatestack 120. Gate stack 120 may include any type of charge storage layeror charge storage medium. Exemplary charge storage layers are describedbelow.

In the current embodiment, substrate 102 is a semiconductor typesubstrate, and is formed to have either P-type or N-type conductivity,at least in channel region 114. Gate contact 118, source contact 104,and drain contact 106 provide electrical connectivity to memory device100. Source contact 104 is formed in contact with source region 112.Drain contact 106 is formed in contact with drain region 116. Source anddrain regions 112 and 116 are typically doped regions of substrate 102that have a conductivity different from that of channel region 114.

As shown in FIG. 1, source contact 104 is coupled to a potential, suchas a ground potential. Drain contact 106 is coupled to another signal.Note that source and drain regions 112 and 116 are interchangeable, andtheir interconnections may be reversed.

FIG. 2 shows a cross-sectional view of gate stack 120, according to oneexemplary embodiment. In FIG. 2, gate stack 120 includes a tunnelingdielectric layer 202, a charge storage layer 204, a charge blockinglayer 206, and a control dielectric layer 208. In the example of FIG. 2,tunneling dielectric layer 202 is formed on channel region 114 ofsubstrate 102 of memory device 100. Charge storage layer 204 is formedon tunneling dielectric layer 202. Charge blocking layer 206 is formedon charge storage layer 204. Control dielectric layer 208 is formed oncharge blocking layer 206. As shown in FIG. 2, gate contact 118 isformed on control dielectric layer 208. Alternatively, the chargeblocking layer 206 may be formed on the control dielectric layer 208,and the gate contact 118 may be formed on the charge blocking layer 206,as shown in FIG. 11. Note that in exemplary embodiments, one or morefurther layers of material may separate the layers of gate stack 120and/or may separate gate stack 120 from substrate 102 and/or gatecontact 118.

Charge storage layer 204 stores a positive or negative charge toindicate a programmed state of memory device 100, as described above.Charge storage layer 204 may include the materials described above, orotherwise known. During programming, a voltage applied to gate contact118 creates an electric field that causes electrons to tunnel (e.g., orvia hot electron injection) into charge storage layer 204 from channelregion 114 through tunneling dielectric layer 202. The resultingnegative charge stored in charge storage layer 204 shifts a thresholdvoltage of memory device 100. The charge remains in charge storage layer204 even after the voltage is removed from gate contact 118. During anerase process, an oppositely charged voltage may be applied to gatecontact 118 to cause electrons to discharge from charge storage layer204 to substrate 102 through tunneling dielectric layer 202 or drawsholes from the channel 114 to tunnel through (or via channel hot holes)the tunnel dielectric layer 202 to the charge storage layer 204. Controldielectric layer 208 isolates the gate contact 118 from the chargeblocking layer 206.

The gate contact 118 is preferably formed of a conductive material. Forexample, the gate contact 118 may be formed of polycrystalline silicon(polysilicon). In another example, the gate contact 118 may be formed ofa metal or a material including one or more metals, such as, forexample, one or more transition metals. Exemplary transition metals thatmay be suitable for the gate contact 118 include, but are not limitedto: Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd,Hf, Ta, W, Re, Os, Ir, Pt, Au, and Hg. According to one exemplaryembodiment, the gate contact 118 may be formed of TaN.

Generally, the thickness of the gate contact 118 is in the range of fromabout 5 nm to about 5,000 nm. Preferably, the thickness is in the rangeof from about 10 nm to about 500 nm. According to one exemplaryembodiment, the gate contact 118 may include a plurality of sublayers.Each sublayer may be formed of a different conductive material.

The gate contact 118 may be formed by vapor deposition techniques knownin the art. Physical vapor deposition (PVD) techniques, such assputtering or thermal evaporation, chemical vapor deposition (CVD), oratomic layer deposition (ALD) may be suitable for deposition of the gatecontact 118.

The charge storage layer 204 may include any type of charge storagemedium. Preferably, the charge storage layer 204 is a localized chargestorage layer that includes a plurality of discrete charge storageelements. The discrete charge storage elements may be one or morelocalized charge traps, such as those found in a nitride layer, orsemiconducting, metallic, or dielectric nanoparticles (quantum dots).For example, charge storage layer 204 may include nanocrystals formed ofa high work function (e.g., greater than 4.5 eV) metal such as ruthenium(Ru), and preferably having a size of less than about 5 nm. Suchnanocrystals may be deposited on tunneling dielectric layer 202 by avariety of processes, such as chemical vapor deposition (CVD), atomiclayer deposition (ALD) or physical vapor deposition (PVD), as is knownin the art. Charge storage layer 204 may also include preformedcolloidal metal or semiconductor or dielectric quantum dots(nanocrystals) deposited on tunneling dielectric layer 202. For example,such materials may be deposited by methods such as spin coating, spraycoating, printing, chemical assembly, nano-imprints using polymerself-assembly and the like, such as described in U.S. Pat. No.6,586,785, U.S. application Ser. No. 11/147,670, and U.S. applicationSer. No. 11/495,188, which are each incorporated by reference herein intheir entirety. Charge storage layer 204 may also include a contiguousmetal or semiconductor conductive layer, a non-contiguous metal orsemiconductor conductive layer, a nonconductive nitride-based or othertypes of insulating charge trapping layer, a nonconductive oxide layer(e.g., SiO₂) having conductive elements disposed therein (e.g., siliconislands), a doped oxide layer, etc. For further description of chargestorage layers that include nitrides, refer to U.S. Pat. No. 5,768,192,which is incorporated by reference herein in its entirety. According toone exemplary embodiment, the charge storage layer may have a U-shapewhen viewed in cross-section along a word line direction of the memorycell.

A surface of tunneling dielectric layer 202 (also referred to as “tunneldielectric layer”) may be altered in order to provide an improvedbarrier to metal migration when metal quantum dots such as ruthenium (orother metal or alloy) are used for the charge storage material. Forexample, as shown in FIG. 3, gate stack 120′ may include a barrier layer302 formed on tunneling dielectric layer 202 between tunnelingdielectric layer 202 and charge storage layer 204. Barrier layer 302 caninclude, for example, a nitrogen containing compound such as nitride(Si₃N₄) or silicon oxynitride (SiO_(x)N_(y), wherein x and y arepositive numbers, 0.8, 1.5, etc., or other suitable barrier layer suchas alumina (Al₂O₃). Barrier layer 302 changes the surface structure oftunneling dielectric layer 202 such that metal migration effects may beminimized. Where barrier layer 302 is made from a nitrogen compound, thenitrogen-containing layer may be formed by adding nitrogen or a“nitrogen-containing” compound (e.g., “nitriding”) to tunnelingdielectric layer 202 (e.g., which may be SiO₂). In an exemplaryembodiment, the nitrogen or nitrogen-containing compound may bedeposited on tunneling dielectric layer 202 using a chemical vapordeposition (CVD) process, such as low pressure CVD (LPCVD) or ultra highvacuum CVD (UHVCVD). The nitrogen-containing layer may be in directcontact with tunneling dielectric layer 202.

UHVCVD of barrier layer 302 may be more controllable than LPCVD, as theUHVCVD generally occurs more slowly, and therefore the growth rate maybe more closely regulated. The nitrogen-containing layer may be formedas a result of deposition from the reaction of such gases as silane (orother silicon source precursor such as dichlorosilane, or disilane) andammonia (or other nitrogen species such as plasma-ionized nitrogen, N₂Oor NO), or a surface reaction to a reacting gas such as ammonia (orother nitrogen species such as plasma-ionized nitrogen, N₂O or NO).Dichlorosilane and ammonia gas in combination with a co-flow of someinert gas and oxygen-containing gas may be used for growth of thenitrogen-containing layer. Barrier layer 302 impedes penetration ofmetal nanoparticles/quantum dots of charge storage layer 204 intotunneling dielectric layer 202, such that contamination of tunneldielectric layer 202, which may result in leakage, is avoided.

A thickness of barrier layer 302 is preferably configured to ensure thatcarrier traps included in nitride structures do not dominate the chargestorage aspects of the semiconductor device being formed. In anexemplary embodiment, a desired thickness for barrier layer 302 is lessthan about 10 angstroms. In further embodiments, the desired thicknessmay be about 5 angstroms or less. The relative thicknesses of tunnelingdielectric layer 202 and barrier layer 302 can be tailored to optimizeelectrical performance and metal migration barrier functions. Thethickness of barrier layer 302 should be at least that required toensure generally uniform coverage of tunneling dielectric layer 202 bybarrier layer 302. Preferably, the barrier layer 302 is at least about 1angstrom in thickness. In an exemplary embodiment where siliconoxynitride is utilized as barrier layer 302, the concentration ofnitrogen within the silicon oxynitride may be greater than about 5%, forexample. A percentage concentration of nitrogen included in the siliconoxynitride can be controlled such that the trade-off between the barrierfunction of the nitrogen layer against metal migration from metalquantum dots (when in charge storage layer 204) and the inclusion oftraps due to nitride concentration is regulated.

In an exemplary embodiment, the tunneling dielectric layer 202 is SiO₂and the substrate 102 is silicon. The control dielectric layer 208 maybe formed of a single component oxide, such as, for example, Al₂O₃ orSiO₂. It is believed that SiO₂ may be advantageous as the controldielectric layer 208 because it poses a high energy barrier to electrontunneling (e.g., see FIG. 4B). Also, SiO₂ contains few charge traps, andit is believed that those present in the layer are sufficiently deepthat they do not hamper the charge retention of the device. According toan alternative embodiment, the control dielectric layer 208 may beformed of a multicomponent material such as a multicomponent oxide.

It is preferred that the control dielectric layer 208 have a thicknessof no more than about 20 nm. The thickness of the control dielectriclayer is believed to be important due to the scaling of new generationsof memory devices to smaller lateral dimensions. As the channel lengthand device width of a memory cell reduce to below about 30 nm, it isdesirable to reduce the thickness of the dielectric layer to less thanthe channel length such that the control gate can maintain the couplingto the charge storage layer. According to an exemplary embodiment, thecontrol dielectric layer 208 is about 15 nm or less in thickness. Thecontrol dielectric layer 208 may also be about 10 nm or less inthickness. According to a preferred embodiment, the control dielectriclayer 208 has a thickness of about 5 nm or less. For example, thecontrol dielectric layer 208 may be about 4 nm or less in thickness,about 3 nm or less in thickness, about 2 nm or less in thickness, orabout 1 nm or less in thickness. It is also preferred that the thicknessof the control dielectric layer 208 is at least that required to ensuregenerally uniform coverage of the underlying layer. Accordingly, thethickness of the control dielectric layer 208 is preferably at leastabout 0.1 nm.

Preferably, the thickness of the control dielectric layer 208 is no morethan about 200% of a thickness of the charge blocking layer 206. Morepreferably, the thickness of the control dielectric layer 208 is no morethan about 150% of the thickness of the charge blocking layer 206. Forexample, according to one exemplary embodiment, the thickness of thecharge blocking layer 206 is about 4 nm, and the thickness of thecontrol dielectric layer 208 is about 5 nm or about 125% of thethickness of the charge blocking layer 206. In other exemplaryembodiments, the thickness of the control dielectric layer 208 is nomore than about 125% of the thickness of the charge blocking layer 206,or no more than about 100% of the thickness of the charge blocking layer206. It is also contemplated that the thickness of the controldielectric layer 208 may be less than the thickness of the chargeblocking layer 206.

In an exemplary embodiment, charge blocking layer 206 is formed of ahigh-k dielectric material. For the purposes of this disclosure, ahigh-k dielectric material has a dielectric constant higher than that ofSiO₂ (e.g., 3.9). The high-k dielectric material of the charge blockinglayer 206 may be, for example, Al₂O₃, HfO₂, HfSiO₂, ZrO₂,Hf_(1-x)Al_(x)O_(Y), where x is a positive number between 0 and 1, and yis a positive number, e.g., HfAlO₃, etc., preferably HfO₂ orHf_(1-x)Al_(x)O_(y), where x is a positive number between 0 and 1, and yis a positive number, e.g., HfAlO₃. In further embodiments, chargeblocking layer 206 may be formed of other high-k dielectric materials,such as Gd₂O₃, Yb₂O₃, Dy₂O₃, Nb₂O₅, Y₂O₃, La₂O₃, ZrO₂, TiO₂, Ta₂O₅,SrTiO₃, BaxSr_(1-x)TiO₃, Zr_(x)Si_(1-x)O_(y), Hf_(x)Si_(1-x)O_(y),Al_(x)Zr_(1-x)O₂ or Pr₂O, for example.

In exemplary embodiments, charge blocking layer 206 has a higherdielectric constant than control dielectric layer 208. For example, inone embodiment, control dielectric layer 208 is Al₂O₃, which has adielectric constant of approximately 9, and charge blocking layer 206 isHfO₂, which has a dielectric constant of less than about 25, e.g.,around 22, when deposited. In another embodiment, control dielectriclayer 208 is SiO₂, which has a dielectric constant of approximately 4,while charge blocking layer is HfO₂.

FIGS. 4A-4C include plots 400, 410, 420 showing schematically howincluding a dielectric layer of a higher dielectric constant (e.g., thecharge blocking layer 206) adjacent to a dielectric layer of a lowerdielectric constant (e.g., the control dielectric layer 208) may improvetunneling resistance. The plot 400 of FIG. 4A shows the energy barrier(eV) of a dielectric layer having a higher dielectric constant (e.g.,HfO₂) alone, and the plot 410 of FIG. 4B shows the energy barrier of adielectric layer having a lower dielectric constant (e.g., SiO₂) alone.The lower k-dielectric layer (SiO₂) provides a higher energy barrier totunneling than does the higher-k dielectric layer (HfO₂), but thehigher-k dielectric layer (HfO₂) provides a wider barrier. The plot 420of FIG. 4C shows the improvement in the magnitude of the tunnelingbarrier when the higher-k dielectric layer (e.g., HfO₂) is disposedadjacent to the lower-k dielectric layer (e.g., SiO₂). Accordingly,tunneling current may be reduced. Any combination of higher-k andlower-k dielectrics may be suitable for the charge blocking layer 206and the control dielectric layer 208. Preferably, as noted above, thecharge blocking layer 206 has the higher dielectric constant (e.g.,lower barrier height), and the control dielectric layer 208 has thelower dielectric constant (e.g., higher barrier height).

In an exemplary embodiment, charge blocking layer 206 may include agradient of composition, band gap value and/or dielectric constantthrough a thickness of the layer 206. The gradient may increase ordecrease from a first surface of charge blocking layer 206 (e.g., asurface of charge blocking layer 206 adjacent to charge storage layer204) to a second surface of charge blocking layer 206 (e.g., a surfaceof charge blocking layer 206 adjacent to control dielectric layer 208).

For example, the charge blocking layer 206 having a gradient ofcomposition may comprise a dielectric material, and an amount of atleast one component of the dielectric material may vary across thethickness of the charge blocking layer 206. Preferably, the dielectricmaterial is a high-k dielectric material. The amount of the componentmay vary linearly, nonlinearly, or step-wise across the thickness of thecharge blocking layer 206. Preferably, the amount of the component is aminimum near the control dielectric layer 208 and increases across thethickness of the charge blocking layer 206. The component may be anelement or a compound. For example, the component may be hafnium orhafnium oxide. According to an exemplary embodiment, the charge blockinglayer 206 having a gradient of composition is formed of a multicomponentdielectric material. For example, the charge blocking layer 206 may beformed of a multicomponent oxide such as, Hf_(x)Al_(1-x)O_(y),Hf_(x)Si_(1-x)O_(y), Zr_(x)Si_(1-x)O_(y), Ba_(x)Sr_(1-x)TiO_(y), orAl_(x)Zr_(1-x)O_(y). The multicomponent dielectric material may includethe component (e.g., hafnium) and a second component, and a ratio of thecomponent to the second component may vary across the thickness of thecharge blocking layer 206, according to an exemplary embodiment. Themulticomponent dielectric material may include nitrogen. For example,the multicomponent dielectric material may beHf_(x)Si_(1-x)O_(2-y)N_(y), according to an exemplary embodiment. Thecharge blocking layer 206 having a gradient of composition may bedisposed between the charge storage layer 204 and the control dielectriclayer 208, or between the control dielectric layer 208 and the gatecontact 118 of the memory device 100.

In another exemplary embodiment, charge blocking layer 206 comprises aplurality of layers of materials. FIG. 5 shows, for example, a chargeblocking layer 206 including three layers. According to this exemplaryembodiment, the charge blocking layer 206 includes a first layer 210closest to the charge storage layer 204, a second (middle) layer 212,and a third layer 214 (furthest from the charge storage layer 204).According to one embodiment, the layer closest to charge storage layer204 is formed of a relatively high band gap material, while the layer(s)further from charge storage layer 204 are formed of material(s) having aprogressively lower band gap. This may be desirable when charge storagelayer 204 comprises isolated particles (e.g., nanoparticles, quantumdots), because a relatively higher band gap material allows lesstunneling between particles than a lower band gap material. SiO₂, Al₂O₃,HfAlO₃ are exemplary materials having relatively high band gap. As oneof ordinary skill in the art would recognize, an alternative embodimentwould include a layer closest to the charge storage layer 204 beingformed of a relatively low band gap material, and layer(s) further fromthe charge storage layer 204 being formed of material(s) having aprogressively higher band gap.

According to an exemplary three-layer embodiment for charge blockinglayer 206, the first layer 210 may be Al₂O₃, the second (middle) layer212 may be HfAlO₃, and the third layer 214 may be HfO₂ (which has arelatively low band gap). In an exemplary two-layer embodiment forcharge blocking layer 206, the first layer (closest to charge storagelayer 204) may be SiO₂, and the second layer may be HfO₂, which has arelatively high dielectric constant (for effective charge blocking) anda low band gap. As described above, control dielectric layer 208 may bea material such as Al₂O₃ or SiO₂.

In an exemplary embodiment, charge blocking layer 206 may be doped. Forexample, charge blocking layer 206 may be doped with dopant materials,such as a rare earth metal, transition metal, silicon, oxygen, ornitrogen. According to one exemplary embodiment, the charge blockinglayer 206 may be Hf_(1-x)Si_(x)O_(2-y)N_(y). The nitrogen may beintroduced by a post deposition nitridation treatment. For example, aHf_(1-x)Si_(x)O₂ layer may be annealed in an environment containing NH₃,N₂O, or NO to form the Hf_(1-x)Si_(x)O_(2-y)N_(y) layer.

In an exemplary embodiment, charge blocking layer 206 is formed to berelatively thin, such as less than about 10 nm, e.g., less than about 5nm, e.g., less than about 2 nm, to reduce trapping of electrons by thehigh dielectric material of charge blocking layer 206. Preferably, thecharge blocking layer 206 has a thickness sufficient to ensure generallyuniform coverage of the underlying layer. For example, the chargeblocking layer 206 may be at least 0.1 nm thick. Preferably, the chargeblocking layer 206 is at least 0.5 nm thick.

FIG. 6 shows another cross-sectional view of gate stack 120″, accordingto an exemplary embodiment. The configuration of gate stack 120″ in FIG.6 is generally similar to FIG. 2, except that in FIG. 6, gate stack 120″further includes a second charge blocking layer 402 formed on controldielectric layer 208. In FIG. 6, gate contact 118 is formed on secondcharge blocking layer 402. In an exemplary embodiment, second chargeblocking layer 402 is formed of a high-k dielectric material, such asAl₂O₃, HfO₂, ZrO₂, Hf_(1-x)Al_(x)O_(y), where x is a positive numberbetween 0 and 1, and y is a positive number, e.g., HfAlO₃,Hf_(1-x)Si_(x)O₂, Hf_(1-x)Si_(x)O_(2-y)N_(y) etc., preferably HfO₂. Thesecond charge blocking layer 402 may be formed of any of the materialsdescribed above for first charge blocking layer 206, and may beconfigured similarly, such as in a single layer configuration (uniformor gradient of material) or multi-layer configuration.

According to an exemplary embodiment in which the second charge blockinglayer 402 includes a gradient of composition, the second charge blockinglayer 402 may comprise a dielectric material, and an amount of at leastone component of the dielectric material may vary across the thicknessof the charge blocking layer 402. Preferably, the dielectric material isa high-k dielectric material. The amount of the component may varylinearly, nonlinearly, or step-wise across the thickness of the secondcharge blocking layer 402. Preferably, the amount of the component is aminimum near the control dielectric layer 208 and increases across thethickness of the second charge blocking layer 402. The component may bean element or compound. For example, the component may be hafnium orhafnium oxide.

According to an exemplary embodiment, the second charge blocking layer402 having a gradient of composition is formed of a multicomponentdielectric material. For example, the second charge blocking layer 402may be formed of a multicomponent oxide such as, Hf_(x)Al_(1-x)O_(y),Hf_(x)Si_(1-x)O_(y), Zr_(x)Si_(1-x)O_(y), Ba_(x)Sr_(1-x)TiO_(y), orAl_(x)Zr_(1-x)O_(y). The multicomponent dielectric material may includethe component (e.g., Hf) and a second component, and a ratio of thecomponent to the second component may vary across the thickness of thesecond charge blocking layer 402, according to an exemplary embodiment.The multicomponent dielectric material may include nitrogen. Forexample, the multicomponent dielectric material may beHf_(x)Si_(1-x)O_(2-y)N_(y), according to an exemplary embodiment. Thesecond charge blocking layer 402 having a gradient of composition may bedisposed between the control dielectric layer 208 and the gate contact118 of the memory device 100, or between the charge storage layer 204and the control dielectric layer 208.

Charge blocking layers 206 and 402, which sandwich control dielectriclayer 208, may efficiently block charge transport through controldielectric layer 208. For example, first charge blocking layer 206(e.g., HfO₂) may block electron current from charge storage layer 204 togate contact 118 during a programming operation. Second charge blockinglayer 402 (e.g., HfO₂) may block electron current from gate contact 118to charge storage layer 402 during an erase operation. In addition, thefirst and/or second charge blocking layers 206, 402 may have otherfunctions. In an exemplary embodiment, the thicknesses of first andsecond charge blocking layers 206 and 402 are thin, such as less than 10nm, e.g., less than 5 nm.

Another advantage of the first and second charge blocking layer 206 and402 is that, although high-k dielectric layers can themselves havetraps, first and second charge blocking layers 206 and 402 can be madevery thin, such as less than about 4 nm, e.g., less than 2 nm, to reducea total amount of charge traps while efficiently blocking current flow.Furthermore, second charge blocking layer 402 is positioned adjacent togate contact 118. Thus, even if a relatively large amount of charge istrapped in second charge blocking layer 402, an effect on the flat-bandvoltage is proportional to a distance from second charge blocking layer402 to gate contact 118, which is minimal (since they may be directlyadjacent to (in contact with) each other).

Some further exemplary advantages of the embodiment of FIG. 6, wherefirst and second charge blocking layers 206 and 402 are HfO₂, andcontrol dielectric layer 208 is Al₂O₃, include:

1) An enhancement in the memory program/erase window may be achieved. Asused herein, a program/erase (P/E) window is the voltage differencebetween threshold states of a program state and an erase state. Withgate stack 120″, memory device 100 can be erased (e.g., up to −6V), witha P/E window of 12.8V or greater. In exemplary embodiments, the P/Ewindow may range from about 8 V to about 16 V (e.g., in ranges of fromabout 9 V to about 14V, about 10 V to about 13V, or have values of about9 V, about 10 V, about 11 V, about 12V, or about 13V). With scaling oftunneling dielectric layer 202 to 6 nm in a +/−20 V P/E limit, the P/Ewindow may be as large as 14.2 V, approaching multi-state memory voltagerequirements, such as for 3-bit or even 4-bit memory cells;

(2) The P/E window may not show significant drift after 100,000 P/Ecycles; and

(3) Charge may be retained in charge storage layer 204 at a 12 V P/Ewindow, and more importantly 100,000 P/E cycles may not degrade thecharge retention characteristics.

In some exemplary embodiments of memory device 100, charge storage layer204 is a single continuous region. For example, FIG. 7 shows a plan viewof charge storage layer 204 having a planar, continuous configuration.For example, charge storage layer 204 may be formed from a continuousfilm of silicon (or polysilicon), a metal, etc. In such a configuration,if a single point of the continuous region breaks down and begins tolose charge, the entire region can lose its charge, causing memorydevice 100 to lose its programmed state. However, some embodiments mayoffer some protection from this problem. For example, FIG. 8 shows aplan view of charge storage layer 204 having a non-continuousconfiguration, according to an exemplary embodiment. In the example ofFIG. 8, charge storage layer 204 comprises a plurality of nanoparticles802. Because nanoparticles 802 of charge storage layer 204 eachseparately store charge, and are insulated from one another, even if asingle nanoparticle loses charge, this will not likely affect theremaining nanoparticles of charge storage layer 204. The same advantagemay be obtained with nonconductive nitride-based charge storage layerswhich store charge in localized charge trap regions. Thus, a memorydevice incorporating a charge storage layer 204 according to the presentdisclosure may maintain a constant programmed state over a much longertime than conventional memory devices.

In an exemplary embodiment, nanoparticles 802 are electrically isolatednanocrystals. Nanocrystals are small clusters or crystals of aconductive material that are electrically isolated from one another.Generally, nanocrystals have a crystallite size of approximately 100 nmor less. One advantage in using nanocrystals for charge storage layer204 is that they do not form a continuous film, and thus charge storagelayers formed of nanocrystals are self-isolating. Because nanocrystalsform a non-continuous film, charge storage layers may be formed withoutconcern about shorting of the charge storage medium of one cell level tothe charge storage medium of adjacent cells lying directly above orbelow (i.e., vertically adjacent). Yet another advantage of the use ofnanocrystals for charge storage layers is that they may experience lesscharge leakage than do continuous film charge storage layers.

Nanocrystals can be formed from conductive material such as palladium(Pd), iridium (Ir), nickel (Ni), platinum (Pt), gold (Au), ruthenium(Ru), cobalt (Co), tungsten (W), tellurium (Te), rhenium (Re),molybdenum (Mo), iron platinum alloy (FePt), tantalum (Ta), tantalumnitride (TaN), etc. Such materials generally have a higher work function(e.g., about 4.5 eV or higher) than many semiconductors such as silicon,which is desirable for multiple electron storage. They may also have ahigher melting point (which allows a higher thermal budget), have longerretention times, and have high density of states for both positive andnegative charge storage.

Methods for forming nanocrystals are well known in the art, for example,as disclosed in U.S. application Ser. No. 11/506,769, filed Aug. 18,2006, the disclosure of which is incorporated herein by reference in itsentirety. A metal nanocrystal charge storage layer can be formed byphysical vapor deposition (PVD) or atomic layer deposition (ALD) inwhich a thin film is first deposited on a surface of a substrate (e.g.,by sputtering using PVD) and then annealed at high temperature (e.g.,about 900 degrees C. or higher) for a short time (e.g., about 10seconds) to coalesce metal particles of nanoscale dimensions. Theuniformity and size of the metal particles can be controlled by varyingthe thickness of the sputtered metal layer, the annealing temperatureand annealing time, pressure, and ambient gas species, etc. When siliconnanocrystals are used in charge storage layer 204, the siliconnanocrystals may be formed by a process such as CVD as described, forexample, in U.S. Pat. No. 6,297,095, which is incorporated by referenceherein in its entirety. Charge storage layer 204 may include preformedcolloidal metal or semiconductor quantum dots deposited on the tunnelingdielectric layer 202 by methods such as spin coating, spray coating,printing, chemical self-assembly and the like. For example, suchprocesses are described in U.S. Pat. No. 6,586,785, U.S. applicationSer. No. 11/147,670, and U.S. application Ser. No. 11/495,188, which iseach incorporated by reference herein in its entirety.

Additionally, instead of including a dielectric isolated charge storagelayer for charge storage in memory device 100, a nonconductive trappinglayer formed in a dielectric stack of the gate stack may be used. Forexample, the charge storage medium can be a dielectric stack comprisinga first oxide layer (e.g., tunneling dielectric layer 202) adjacent tochannel region 114, a nonconductive nitride layer adjacent to the firstoxide layer, and a second oxide layer adjacent to the nitride layer andadjacent to gate contact 118. Such a dielectric stack is sometimesreferred to as an ONO stack (i.e., oxide-nitride-oxide) stack. Thesecond oxide layer can be replaced with one of gate stacks 120, 120′, or120″ to improve the performance of the traditional ONO stack. Othersuitable charge trapping dielectric films such as an H+ containing oxidefilm can be used if desired.

EXEMPLARY EMBODIMENTS

In an exemplary embodiment, charge storage layer 204 includes metaldots, charge blocking layer 206 is HfO₂, and control dielectric layer208 is Al₂O₃. FIG. 9A shows a simulation plot 900 of energy (eV) versusa thickness (nm) for a combination control dielectric of charge blockinglayer 206 (HfO₂) and control dielectric layer 208 (Al₂O₃). FIG. 9B showsa simulation plot 920 of current (A/cm²) versus electric field (V/cm).The plot includes a plot line 902 for the combination control dielectricincluding only HfO₂, and a plot line 904 for the combination controldielectric including only Al₂O₃. For both of plot lines 902 and 904, nobarrier lowering is indicated. The data in FIGS. 9A and 9B show thatincluding a thin layer of HfO₂ at the interface of metal and Al₂O₃ canreduce the electron tunneling current by many orders of magnitude. Thisis true even if the HfO₂ layer is less than 1 nm thick.

FIGS. 10A-10C show plots 1000, 1010, and 1020 related to an exemplarygate stack similar to gate stack 120 shown in FIG. 2. As shown in FIG.10B, an erase voltage is approximately −3.7V and a program voltage isapproximately 9.3V, for a total P/E window of 13 V.

FIGS. 11A and 11B show plots 1100, 1120 of program and erase voltagesfor an exemplary gate stack similar to gate stack 120″ shown in FIG. 6.In this example, charge storage layer 204 is formed of quantum dots,first charge blocking layer 206 is formed of HfO₂ having a thickness of4 nm, control dielectric layer 208 is formed of Al₂O₃ at a thickness of12 nm, and second charge blocking layer 402 is formed of HfO₂ at athickness of 4 nm. As indicated by the data in FIGS. 11A and 11B, a P/Elinear window is approximately 11.39V.

FIGS. 11C and 11D respectively show plots 1130 and 1140 of program anderase voltages for an exemplary gate stack similar to gate stack 120″shown in FIG. 6. In this example, charge storage layer 204 is formed ofquantum dots, first charge blocking layer 206 is formed of HfO₂ having athickness of 4 nm, control dielectric layer 208 is formed of Al₂O₃ at athickness of 12 nm, and second charge blocking layer 402 is formed ofHfO₂ at a thickness of 8 nm. As indicated by the data in FIGS. 11C and11D, a P/E linear window is approximately 12.76V.

FIGS. 11E and 11F show plots 1150 and 1160, respectively, obtained fromcharge retention tests of memory devices including four exemplary gatestacks similar to gate stack 120″ shown in FIG. 6. According to firstand third embodiments (1152, 1156) of the gate stack, first chargeblocking layer 206 is formed of HfO₂ of 2 nm in thickness that hasundergone a nitridation treatment; control dielectric layer 208comprises Al₂O₃ of 16 nm in thickness; and second charge blocking layer402 is formed of HfO₂ of 2 nm in thickness that has undergone anitridation treatment. According to second and fourth embodiments (1154,1158) of the gate stack, first charge blocking layer 206 is formed ofHfO₂ of 4 nm in thickness that has undergone a nitridation treatment;control dielectric layer 208 comprises Al₂O₃ of 12 nm in thickness; andsecond charge blocking layer 402 is formed of HfO₂ of 4 nm in thicknessthat has undergone a nitridation treatment. In the first and secondembodiments (1152, 1154), the nitridation treatment entails an ammonia(NH₃) anneal followed by a rapid thermal anneal (RTA) in nitrogen, andin the third and fourth embodiments (1156, 1158) the nitridationtreatment entails just the RTA in nitrogen. The ammonia anneal wascarried out at 900° C. for 1 h at an ammonia pressure of 250 mTorr, andthe RTA was carried out in flowing nitrogen at 950° C. for 20 s.Alternatively, the nitridation treatment may be carried out in anitrogen plasma. Having undergone the nitridation treatment, all or aportion of the first and second charge blocking layers 206, 402 of theexemplary embodiments may include hafnium oxynitride (HfON).

The samples were prepared on a substrate including an 80 Å SiO₂ tunneloxide layer. The charge storage layer 204 of the four exemplary gatestacks in the examples of FIGS. 11E and 11F includes metal nanocrystals,but alternatively the charge storage layer 204 may be a nitride layer ora polycrystalline silicon (polysilicon) layer, as described previously.In the case of a nitride charge storage layer, a dual layer dielectricstructure including just the first charge blocking layer 206 and thecontrol dielectric layer 208, as shown for example in FIGS. 2 and 12,may be advantageous.

To carry out the charge retention tests, the memory devices includingthe exemplary gate stacks are initially programmed to approximately 4Vand then baked (heated) at 250° C. for up to 24 hours. Under theseconditions, the memory devices undergo an accelerated reliability testthat allows the charge loss that would occur over a much longer period(e.g., up to ten years) at room temperature to be simulated.

FIG. 11E shows flatband voltage V_(FB) as a function of bake time inseconds, where data were obtained from each memory device at the start,after 60 seconds, after 600 seconds, and after 3,600 seconds (1 hour).The memory devices including the gate stacks that were nitrided inammonia (the first and second embodiments) show the best chargeretention. Of these two embodiments, the memory device including thegate stack having a 16 nm Al₂O₃ layer sandwiched between two 2 nm HfO₂layers (first embodiment; curve 1152) had the higher charge retentionwith a charge loss (ΔV_(FB)) of about 0.1 V at 250° C. for 1 h. Thememory device including the 12 nm Al₂O₃ layer sandwiched between two 4nm HfO₂ layers (second embodiment of the gate stack; curve 1154) showedthe second best charge retention with a charge loss of about 0.7 V at250° C. for 1 h.

The memory devices including the gate stacks that underwent only the RTAin nitrogen (third and fourth embodiments) show higher charge losses. Ofthese two embodiments, the memory device including the gate stack havinga 12 nm Al₂O₃ layer sandwiched between two 4 nm HfO₂ layers (fourthembodiment; curve 1158) had the lowest charge retention of all fourdevices with a charge loss of about 1 V at 250° C. for 1 h. The thirdembodiment of the gate stack (curve 1156), with a 16 nm Al₂O₃ layersandwiched between two 2 nm HfO₂ layers, exhibited a charge loss ofabout 0.8 V at 250° C. for 1 h.

Referring now to FIG. 11F, the charge retention of the memory deviceincluding the first embodiment of the gate stack, which includes the 16nm Al₂O₃ layer sandwiched between two 2 nm HfO₂ layers that underwentthe ammonia anneal and then the RTA, was evaluated over a 24 h period atthe same test temperature of 250° C. The memory device exhibited acharge loss (ΔV_(FB)) of 0.32 V over the duration of the test.

Preferably, the memory device exhibits a charge loss of about 0.5 V orless over a period of 24 hours at 250° C. In addition, the memory devicepreferably exhibits a charge retention of about 85% or greater. Morepreferably, the memory device exhibits a charge retention of about 90%or greater.

The inventors believe that the inclusion of nitrogen in the HfO₂ layersserves to densify the high K dielectric, thereby reducing the trapdensity and the rate of charge leakage. The data indicate that thethickness of the layers also plays a role in the charge retentioncapability of the device. Preferably, the control dielectric layer 208has a thickness of from about 6 times to about 10 times that of thefirst and second charge blocking layers 206, 402. It may beadvantageous, for example, for the control dielectric layer 208 to havea thickness of from about 4 nm to about 18 nm, or from about 8 nm toabout 16 nm, and for each of the first and second charge blocking layers206, 402 to have a thickness of from about 1 nm to about 6 nm, or fromabout 1 nm to about 3 nm.

In the preceding examples, the oxynitride layers were formed bynitriding hafnium oxide layers deposited by atomic layer deposition or asimilar technique. It is also contemplated that the oxynitride mayinclude a component other than hafnium and may be formed by nitriding anoxide other than hafnium oxide. For example, the oxynitride may be asilicon oxynitride formed by nitriding silicon oxide. Generallyspeaking, the oxynitride may include a component M (MO_(2-y)N_(y)),where M is selected from the group consisting of, for example, Hf, Si,and Al. The oxynitride may also include more than one component (e.g., Mand M′) in addition to oxygen and hydrogen; for example, the component Mmay be present at a concentration x and M′ may be present at aconcentration of 1−x: M_(x)M′_(1-x)O_(2-y)N_(y). According to thisembodiment, for example, M may be Hf and M′ may be Si, and theoxynitride may be Hf_(x)Si_(1-x)O_(2-y)N_(y).

If the nitridation treatment (e.g., ammonia anneal) is carried out afterall of the layers of the gate stack are deposited, then the secondcharge blocking layer 402 may include an excess of nitrogen compared tothe first charge blocking layer 206. Accordingly, it may be advantageousto carry out a nitridation treatment after the first charge blockinglayer 206 is deposited and before the second charge blocking layer 402is deposited, and then to repeat the nitridation treatment after formingthe second charge blocking layer 402. Using this processing approach,the first and second charge blocking layers 208, 402 may contain similaramounts of nitrogen.

For example, referring again to FIG. 6, a layer of HfO₂ may be depositedas the first charge blocking layer 206 on the charge storage layer 204of the gate stack 120″. Prior to depositing additional layers, thedevice may be placed in a furnace and annealed in, for example, 250mTorr of ammonia for 1 h at about 900° C. As a result of thisnitridation treatment, an oxynitride (HfON) may be formed from some orall of the oxide (HfO₂) of the first charge blocking layer 206. Then,the control dielectric layer 208 (e.g., Al₂O₃) and the second chargeblocking layer 402 (e.g., HfO₂) may be deposited by ALD or anothertechnique, and the nitridation treatment can be repeated to form anoxynitride from the oxide of the second charge blocking layer 402. Forexample, the device may be returned to the furnace and annealed inammonia for 1 h at 900° C. as described previously. Consequently, HfONmay be obtained from some or all of the HfO₂ of the second chargeblocking layer 402, as well as from some or all of the first chargeblocking layer 206. It may also be advantageous as a final step to placethe ammonia-annealed device in a tube configured for flowing nitrogen toperform a rapid thermal anneal (RTA) at a temperature of about 1000° C.for about 10-30 seconds. The RTA may be effective in driving hydrogenout of the gate stack. In the case of a gate stack including only onecharge blocking layer adjacent to the control dielectric layer, morethan one nitridation treatment may not be necessary.

As described above, the ammonia anneal is preferably carried out at atemperature of about 900° C. or less. For example, the anneal may becarried out at a temperature of about 850° C. or less, or at atemperature of about 800° C. or less. Preferably, the temperature of theammonia anneal is at least about 750° C. The duration of the ammoniaanneal is preferably about 60 minutes, although any time in the range offrom about 50 minutes to about 70 minutes may be suitable for thenitridation treatment. Generally speaking, a rapid thermal anneal inammonia may be carried out at higher temperatures and shorter times thana furnace anneal in ammonia.

In another exemplary embodiment, the gate stack of the memory device mayinclude a nitride layer as the charge storage layer, an Al₂O₃ layer asthe control dielectric layer, and a hafnium containing compound such asHfO₂ as the charge blocking layer. As shown in FIG. 12, the chargeblocking layer 206 may be formed above the control dielectric layer 208and adjacent the control gate 118 according to this embodiment. As notedabove, the gate stack may include one (or more) other charge blockinglayers, such as a charge blocking layer below the control dielectriclayer and adjacent the nitride layer. FIG. 13 shows a chart 1300 oferase time (x-axis) versus flat-band voltage (y-axis) comparing aconventional gate stack (reference numeral 1304) without one (or more)charge blocking layers, versus an improved gate stack (reference numeral1302) described above using a nitride layer as the charge trapping layerand a charge blocking layer (e.g., HfO₂) formed adjacent to the controldielectric layer (e.g., Al₂O₃). FIG. 14 shows a chart 1400 comparing thenumber of program and erase cycles (x-axis) versus the flat-band voltage(y-axis) using the improved gate stack represented by reference numeral1302 in FIG. 13. FIG. 14 shows a chart of room temperature chargeretention mapping time (x-axis) versus flat-band voltage (y-axis) usingthe improved gate stack.

As first shown in FIG. 13, the use of the improved gate stack 1302comprising charge blocking layer (e.g., HfO₂) formed over the controldielectric layer (e.g., Al₂O₃) with a nitride charge trapping layershows an enhancement in the memory P/E window (e.g., on the order ofabout 2 volts or greater) compared to conventional gate stack 1304including only an Al₂O₃ control dielectric layer without a chargeblocking layer. Such a memory device with the improved gate stack has atotal P/E window of greater than about 8 volts, which is believed to bethe highest P/E window reported in the literature to date using anitride layer as the charge trapping layer. In addition, as shown in theplot 1400 of FIG. 14, the P/E window does not show significant driftafter 100,000 P/E cycles using the improved gate stack embodiment. And,as shown in the plot 1500 of FIG. 15, the charge is retained at greaterthan an 8V P/E window using the improved gate stack, and 100,000 P/Ecycles do not degrade the charge retention characteristics of the memorydevice.

In another exemplary embodiment, the charge blocking layer 206 is HfO₂and the control dielectric layer 208 is SiO₂. FIG. 16A shows asimulation plot 1600 of energy (eV) versus thickness (nm) for variousdielectric layers, including SiO₂ alone (data line 1602), HfO₂ alone(data line 1604), and combinations of HfO₂ with SiO₂ (data lines 1606,1608, 1612, 1614). FIG. 16B shows a simulation plot 1610 ofFowler-Nordheim tunneling current density (A/cm²) versus electric field(V/cm) for the same dielectric layers. The calculated data show thatincluding a thin layer of HfO₂ at an interface between a conductor(e.g., a metal having a work function of 4.8 eV) and SiO₂ can reduceelectron tunneling by several orders of magnitude.

In another exemplary embodiment, the charge blocking layer 206 isHf_(x)Si_(1-x)O₂ and the amount (x) of Hf varies across the thickness(z) of the charge blocking layer, as shown in plot 1700 of FIG. 17A. Inthis figure, the amount of Hf decreases away from the interface (z=0) ina nonlinear fashion. The optimal composition and thickness of the chargeblocking layer to suppress electron tunneling depend on the electricfield strength. The data were optimized for an electric field strength(E_(SiO2)) of 20 MV/cm. FIG. 17B shows a simulation plot 1710 of barrierheight (eV) versus distance (z) from the interface for theHf_(x)Si_(1-x)O₂ layer of varying Hf content compared to the barrierheight for HfO₂ and SiO₂ layers. Similarly, FIG. 17C shows a simulationplot 1720 of the variation in dielectric constant (O) across the layer(z) for the Hf_(x)Si_(1-x)O₂ layer of varying Hf content. Dielectricconstants of the HfO₂ and SiO₂ layers are also shown. The data lines forHf_(x)Si_(1-x)O₂, HfO₂, and SiO₂ are represented by reference numerals1702, 1704, and 1706, respectively.

Plot 1800 in FIG. 18 shows how the optimal Hf content (x) of theHf_(x)Si_(1-x)O₂ layer varies as a function of voltage for a givenelectric field strength.

Plot 1900 of FIG. 19A shows optimal Hf contents (x) for various electricfield strengths across a charge blocking layer/control dielectriclayer/charge blocking layer structure of the following composition:Hf_(x)Si_(1-x)O₂/SiO₂/Hf_(x)Si_(1-x)O₂. Data lines 1902, 1904, 1906, and1908 correspond respectively to electric field strengths of 15 MV/cm, 20MV/cm, 25 MV/cm, and 30 MV/cm. For an equivalent oxide thickness (EOT)of 7 nm, the optimal film composition is roughly Hf_(2/3)Si_(1/3)O₂ (4.5nm)/SiO₂ (5 nm)/Hf_(2/3)Si_(1/3)O₂ (4.5 nm) at an electric fieldstrength of 20 MV/cm.

Plot 1910 of FIG. 19B shows Fowler-Nordheim tunneling current density asa function of electric field strength for the same layer structure andcomposition as in FIG. 19A, and also for SiO₂, HfO₂, and for HfO₂ (4nm)/SiO₂ (5.4 nm)/HfO₂ (4 nm) (data lines 1912, 1914, and 1916,respectively). Tunneling current can be reduced by over two orders ofmagnitude by using a compositionally graded dielectric as the chargeblocking layer. The data show that tunneling current may be maintainedat less than about 10⁻⁴ A/cm² at an electric field strength that isequivalent to an electric field strength of 2.5×10⁷ V/cm in SiO₂.Accordingly, a total dynamic linear range of a memory device may beextended to ±10V with Vg˜±25V using an optimized charge blocking layer.

Plots 1920 and 1930 of FIGS. 19C and 19D, respectively, show energy banddiagrams calculated for various electric field strengths for theabove-mentioned layer structures and compositions.

Various data presented in the previous figures were calculated using theWentzel-Kramers-Brillouin (WKB) approximation, where ψ(x) represents thewave function in the tunnel barrier and κ(z) represents the imaginarypart of the wave vector:

${{\left. {\psi(x)} \right.\sim{\exp\left\lbrack {- {\int_{0}^{{\kappa{(z)}} = 0}{{\kappa(z)}{\mathbb{d}z}}}} \right\rbrack}}\mspace{14mu}{\kappa(z)}} = {\frac{1}{\hslash}\sqrt{2{{m_{eff}(z)}\left\lbrack {{\varphi(z)} - {V(z)} - E_{F}} \right\rbrack}}}$

To minimize the tunneling current ψ(x),

∫₀^(κ(z) = 0)κ(z)𝕕zis maximized.

$\begin{matrix}{{\int_{0}^{{\kappa{(z)}} = 0}{{\kappa(z)}{\mathbb{d}z}}} = {\frac{1}{\hslash}{\int_{0}^{{{{\varphi{(z)}}{V{(z)}}} - E_{F}} = 0}{\sqrt{2{{m_{eff}(z)}\left\lbrack {{\varphi(z)} - {V(z)} - E_{F}} \right\rbrack}} \times {\mathbb{d}z}}}}} \\{= {\frac{1}{\hslash}{\int{\sqrt{2{{m_{eff}(z)}\left\lbrack {{\varphi(z)} - {V(z)} - E_{F}} \right\rbrack}} \times \frac{\mathbb{d}{V(z)}}{E(z)}}}}} \\{= {\frac{1}{\hslash\; E_{{SiO}\; 2}ɛ_{{SiO}\; 2}}{\int_{0}^{{\varphi{(z)}} - E_{F}}{\sqrt{2{{m_{eff}(z)}\left\lbrack {{{\varphi(z)}{V(z)}} - E_{F}} \right\rbrack} \times {ɛ^{2}(z)}} \times}}}} \\{\mathbb{d}{V(z)}}\end{matrix}$

Thus, √{square root over (2m_(eff)(z)[φ(z)−V(z)−E_(F)]×∈²(z))}{squareroot over (2m_(eff)(z)[φ(z)−V(z)−E_(F)]×∈²(z))}{square root over(2m_(eff)(z)[φ(z)−V(z)−E_(F)]×∈²(z))}{square root over(2m_(eff)(z)[φ(z)−V(z)−E_(F)]×∈²(z))} is maximized for each V(z). For amaterial M including components A and B, where x represents theproportion of A and (1−x) is the proportion of B, e.g., M=x×A+(1−x)×B,needed material constants may be obtained by linear superposition. Forexample, a dielectric constant ∈ of the material M may be obtained from∈=x×∈_(A)+(1−x)×∈_(B). An effective mass m_(eff) of the material M maybe obtained from m_(eff)=x×m_(eff,A)+(1−x)×m_(eff,B). Electron affinityφ may be obtained from φ=x×φ_(A)+(1−x)×φ_(B). E_(F) is the Fermi energy.

It is believed that the above-described calculation procedure is usefulfor predicting the behavior of dielectric layers, gate stacks, and/ormemory devices described herein; however, this calculation procedureshould not be used to limit the scope of the present invention.

Multistate Memory Embodiments

A memory device may have any number of memory cells. In a conventionalsingle-bit memory cell, a memory cell assumes one of two informationstorage states, either an “on” state or an “off” state. The binarycondition of “on” or “off” defines one bit of information. As a result,a conventional memory device capable of storing n-bits of data requires(n) separate memory cells.

The number of bits that can be stored using single-bit per cell memorydevices depends upon the number of memory cells. Thus, increasing memorycapacity requires larger die sizes containing more memory cells, orusing improved photolithography techniques to create smaller memorycells. Smaller memory cells allow more memory cells to be placed withina given area of a single die.

An alternative to a single-bit memory cell is a multi-bit or multistatememory cell, which can store more than one bit of data. A multi-bit ormultistate flash memory cell may be produced by creating a memory cellwith multiple, distinct threshold voltage levels, V_(t1-n), asdescribed, for example, in U.S. Pat. No. 5,583,812, which isincorporated by reference herein in its entirety. Each distinctthreshold voltage level, V_(t1-n), corresponds to a value of a set ofdata bits, with the number of bits representing the amount of data thatcan be stored in the multistate memory cell. Thus, multiple bits ofbinary data can be stored within the same memory cell.

Each binary data value that can be stored in a multistate memory cellcorresponds to a threshold voltage value or range of values over whichthe multistate memory cell conducts current. The multiple thresholdvoltage levels of a multistate memory cell are separated from each otherby a sufficient amount so that a level of a multistate memory cell canbe programmed or erased in an unambiguous manner. The specificrelationship between the data programmed into the memory cell and thethreshold voltage levels of the cell depends upon the data encodingscheme adopted for the multistate memory cell.

In programming a multistate memory cell, a programming voltage isapplied over a sufficient time period to store enough charge in thecharge storage layer to move the multistate memory cell's thresholdvoltage to a desired level. This level represents a state of themultistate memory cell, corresponding to an encoding of the dataprogrammed into the multistate memory cell.

According to various exemplary embodiments, multiple threshold voltagelevels for a multistate memory cell/device may be provided in chargestorage layer 204 by electrically isolated nanoparticles (such as shownin FIG. 8) or a contiguous or non-contiguous metal (or silicon) layersuch as shown in FIG. 7.

In another embodiment of multi-bit memory cells, as described forexample in U.S. Pat. No. 5,768,192, which is incorporated by referenceherein in its entirety, charge is stored in a non-conductive chargetrapping layer (e.g., a nitride layer) in two physically distinctregions on opposite sides of the memory cell near the source and drainregions of the device. By developing symmetric and interchangeablesource and drain regions in the cell, two non-interactive physicallydistinct charge storage regions are created, with each region physicallyrepresenting one bit of information mapped directly to the memory arrayand each cell thereby containing two bits of information. Programming ofthe cell is performed in a forward direction which includes injectingelectrical charge into the charge trapping material within the gateutilizing hot electron injection for a sufficient time duration suchthat electrical charge becomes trapped asymmetrically in the chargetrapping material, the electrical charge being injected until thethreshold voltage of the gate reaches a predetermined level. The cell isthen read in the reverse direction from which it was programmed. Thistype of multi-bit memory cell can also be extended to charge storagelayer memory devices using discrete metal nanocrystals as the chargestorage medium, as described, for example, in U.S. Appl. Pub. No.2004/0130941, which is incorporated by reference herein in its entirety.

The present inventors have also discovered that multi-bit storage usingasymmetrical charge storage as described above can be accomplished usingcolloidal metal nanocrystals (e.g., as described in U.S. Pat. No.6,586,785 and in U.S. application Ser. Nos. 11/147,670 and 11/495,188).The tighter control of the size and uniformity of such colloidal metaldots (e.g., over other deposited nanocrystals using PVD or CVD) has theadvantage of relaxing the requirement on threshold spread by minimizinglateral charge conduction between adjacent dots when selectivelycharging a small portion of the nanocrystals near the source and/ordrain of the device to produce the charging asymmetry.

A significant feature of the use of the devices and methods describedherein is that they may enable the reliable storage of multiple bits ina single device using, e.g., any of the conventional techniques forgenerating multi-state memory as described herein. Conventional flashmemories using multi-bit storage achieved through the above-describedmethods such as the multi-level approach suffer from the stringentrequirements on the control of the threshold spread. The presentexemplary embodiments, however, may overcome many of the limitations ofconventional flash memory devices by providing a large programming/erasewindow (on the order of, e.g., 8 volts or greater, or 12 volts orgreater), increased programming/erasing speed and good charge retention.This may allow for a greater separation between the various thresholdvoltage states from each other so that a level of a multistate memorycell can be programmed or erased in an unambiguous manner.

The present embodiments may also further enable the storage of multiplebits, such as three or more (e.g., four) bits per cell by, e.g., storingcharge in each of two different storage locations in the charge storagelayer and further adding the ability to store different quantities orcharge states in each of the two locations using e.g., multiple voltagethreshold levels as described above. The charge storage layer may be,for example, a nanocrystal layer or a non-conductive nitride layer, asdescribed above. By storing four different quantities of charge at eachlocation the memory device can thereby store 4×4=16 differentcombinations of charge providing the equivalent of four bits per cell.The enhancement in program/erase window provided by the teachingsdescribed herein without compromising charge retention may furtherenable multi-bit storage capability by providing greater flexibility inthe injection and detection of charge in the storage medium and arelaxed requirement on threshold spread.

The exemplary embodiments described herein may be assembled according towell known semiconductor manufacturing techniques. FIG. 20 shows aflowchart 2000 providing an exemplary procedure for forming anelectronic device, such as a memory device. Flowchart 2000 is providedfor illustrative purposes, but is not intended to be limiting. Furtherstructural and operational embodiments will be apparent to personsskilled in the relevant art(s) based on the following discussion. Theprocedure of flowchart 2000 does not necessarily have to be followed inthe order shown.

Flowchart 2000 begins with formation of a source region in a substrate2002. For example, as shown in FIG. 1, source region 112 may be formedin substrate 102. Source region 112 may be formed according toconventional doping or other techniques. Furthermore, in an exemplaryembodiment, source contact 104 may be formed on source region 112according to conventional deposition or other techniques.

Next, a drain region may be formed in the substrate 2004. For example,as shown in FIG. 1, drain region 116 may be formed in substrate 102.Drain region 116 may be formed according to conventional doping or othertechniques. Furthermore, in an embodiment, drain contact 106 may beformed on drain region 116 according to conventional deposition or othertechniques.

A tunneling dielectric layer may be formed on the substrate 2006. Forexample, as shown in FIGS. 2 and 6, tunneling dielectric layer 202 maybe formed on channel region 114 of substrate 102. Tunneling dielectriclayer 202 may be formed according to conventional oxide growth or othertechniques.

A charge storage layer may be formed on the tunneling dielectric layer2008. For example, as shown in FIGS. 2 and 6, charge storage layer 204may be formed over tunneling dielectric layer 202. In an exemplaryembodiment, charge storage layer 204 is formed directly on tunnelingdielectric layer 202. In another embodiment, charge storage layer 204 isformed on an intermediate layer formed on tunneling dielectric layer202, such as barrier layer 302 shown in FIG. 3.

Charge storage layer 204 may be a metal or semiconductor material layer(continuous or non-continuous) or a layer of particles, such as furtherdescribed above. Charge storage layer 204 may be formed by depositiontechniques such as physical vapor deposition (PVD), chemical vapordeposition (CVD), electrochemical deposition (ECD), molecular beamepitaxy (MBE), atomic layer deposition (ALD), or other techniquesdescribed elsewhere herein or otherwise known.

The charge blocking layer may be formed on the charge storage layer2010. For example, as shown in FIGS. 2 and 6, charge blocking layer 206is formed over charge storage layer 204. Charge blocking layer 206 maybe formed according to any deposition technique described elsewhereherein or otherwise known, such as by atomic layer deposition. In anexemplary embodiment, as described above, charge blocking layer 206 maybe doped. Furthermore, in another exemplary embodiment, as describedabove, charge blocking layer 206 may be formed as a gradient or ashaving multiple layers.

Atomic layer deposition may be particularly suitable for forming acharge blocking layer 206 including a composition gradient or multiplelayers. For example, to form a charge blocking layer 206 composed of adielectric material having a component that varies in concentrationacross a thickness of the charge blocking layer 206, one or more firstmonolayers of the dielectric material may be deposited using a firstprecursor of a first chemistry, and then one or more second monolayersof the dielectric material may be deposited using a second precursor ofa second chemistry, and then one or more third monolayers of thedielectric material may be deposited using a third precursor of a thirdchemistry, etc. In other words, consecutive depositions of one or moremonolayers may be carried out using different precursors in order toform the charge blocking layer 206 including either a compositiongradient or multiple layers. It is also envisioned that a chargeblocking layer 206 of a uniform composition may be deposited initiallyand then a rapid thermal anneal (RTA) may be employed to achieve theeffect of a compositionally graded layer.

A control dielectric layer may be formed on the charge blocking layer2012. For example, as shown in FIGS. 2 and 6, control dielectric layer208 is formed over charge blocking layer 206. Control dielectric layer208 may be formed according to any deposition technique describedelsewhere herein or otherwise known, such as by atomic layer deposition.

A second charge blocking layer may be formed over the control dielectriclayer 2014. As shown in FIG. 6, second charge blocking layer 402 isformed over control dielectric layer 208. Second charge blocking layer402 may be formed according to any deposition technique describedelsewhere herein or otherwise known, such as atomic layer deposition. Inan embodiment, in a similar fashion to first charge blocking layer 206,second charge blocking layer 402 may be doped. Furthermore, in anembodiment, in a similar fashion to first charge blocking layer 206,second charge blocking layer 402 may be formed as a gradient or ashaving multiple layers.

The second charge blocking layer 402 is not necessarily formed in allembodiments. For example, FIG. 2 shows a gate stack 120 that does notinclude a second charge blocking layer. In another example, as shown inFIG. 11, the gate stack 120 may include the charge blocking layer 206 onthe control dielectric layer 208, and a second charge blocking layer maynot be formed.

A control gate may be formed over the gate stack 2016. For example, asshown in FIG. 2, gate contact 118 is formed over control dielectriclayer 208 of gate stack 120. As shown in FIG. 6, gate contact 118 isformed over second charge blocking layer 402 of gate stack 120″. Gatecontact 118 may be formed on gate stacks 120 and 120″ according toconventional deposition or other techniques.

Methods, systems and apparatuses for improved electronic devices, suchas memory devices that may have enhanced characteristics, includingincreased charge retention, enhanced memory program/erase window,improved reliability and stability, with feasibility for single ormultistate (e.g., two, three or four bit) operation, have been describedherein.

The use of a multi-layer control dielectric, such as a double or triplelayer control dielectric, in a nonvolatile memory device has beendisclosed. The multi-layer control dielectric may include a combinationof high-k dielectric materials such as aluminum oxide (Al₂O₃), hafniumoxide (HfO₂), and/or hybrid films of hafnium aluminum oxide (HfAlO_(x),wherein x is a positive integer, e.g., 1, 2, 3, 4, etc.) therein.

A double control dielectric layer for a memory device has beendescribed, including, for example, a control dielectric layer of Al₂O₃,and a charge blocking layer of HfO₂ (or Hf_(1-x)Al_(x)O_(y), where x isa positive number between 0 and 1, and y is a positive number, e.g.,HfAlO₃). The layer of HfO₂ may provide an efficient charge blockinglayer to block electron current flow from the charge storage layer tothe control gate during a programming operation of the memory device.

A double control dielectric layer for a memory device including, forexample, a control dielectric layer of Al₂O₃ and a layer of a hafniumcontaining compound such as HfO₂ between the control dielectric and thecontrol gate has also been disclosed. The layer of HfO₂ may suppress atunneling current from a control gate of the memory device during eraseoperations which can lead to large over-erase voltages.

A double control dielectric layer for a memory device including, forexample, a control dielectric layer of Al₂O₃ and a layer of a hafniumcontaining compound such as HfO₂ between the control dielectric and thecharge storage layer has also been disclosed. The layer of HfO₂ maysuppress a tunneling current from the charge storage layer of the memorydevice to the control gate during programming operations.

A triple control dielectric layer for a memory device also has beendescribed. For example, the triple control dielectric layer may includea first layer of a hafnium containing compound such as HfO₂ (orHf_(1-x)Al_(x)O_(y), where x is a positive number between 0 and 1, and yis a positive number, e.g., HfAlO₃) adjacent to the charge storage layerof the device, a second layer of a hafnium containing compound such asHfO₂ adjacent to the control gate of the memory device, and a layer ofAl₂O₃ between the first and second layers of HfO₂. The second layer ofHfO₂ may block electron current from the control gate to the chargestorage layer during the erase operation of the memory device.

The thickness of single or dual layers of the charge blocking layer maybe kept very thin while still efficiently blocking current flow. Forexample, in an embodiment, the thickness is less than about 10 nm e.g.,less than about 5 nm, e.g., less than about 4 nm. In another exampleembodiment, the thickness is less than about 2 nm. Preferably, thethickness is greater than about 0.1 nm

The use of such a double or triple layer control dielectric may providethe unexpected result of achieving a very large program/erase window(e.g., on the order of at least 8 volts or greater, for example, about 9volts, e.g., about 10 volts, e.g., about 11 volts, e.g., about 12 voltsor greater), while still providing for good charge retention andprogramming/erasing speed, which is important in making reliablemulti-bit/cell memory devices with scaling to smaller node sizes.Furthermore, the charge blocking layer may dramatically reduce theamount of current that flows through the control dielectric during theprogram, erase, and read operations, which may enable flash memorydevices that can endure a large number of program/erase cycles withoutsignificant drift in operation voltages.

In exemplary embodiments, various high-k dielectric materials, such asGd₂O₃, Yb₂O₃, Dy₂O₃, Nb₂O₅, Y₂O₃, La₂O₃, ZrO₂, TiO₂, Ta₂O₅, SrTiO₃,Ba_(x)Sr_(1-x)TiO₃, Zr_(x)Si_(1-x)O_(y), Hf_(x)Si_(1-x)O_(y),Hf_(x)Si_(1-x)O_(2-y)N_(y), Al_(x)Zr_(1-x)O₂, or Pr₂O, for example, maybe used for the charge blocking layer.

A charge blocking layer including a composition gradient across thethickness of the charge blocking layer also has been described herein.For example, the charge blocking layer may be made of a dielectricmaterial, and an amount of at least one component of the dielectricmaterial may vary across the thickness of the charge blocking layer. Forexample, the component may be hafnium or hafnium oxide. According to anexemplary embodiment, the charge blocking layer having a compositiongradient may be formed of a multicomponent oxide such as, for example,Hf_(x)Al_(1-x)O_(y), Hf_(x)Si_(1-x)O_(y), Zr_(x)Si_(1-x)O_(y),Ba_(x)Sr_(1-x)TiO_(y), and Al_(x)Zr_(1-x)O_(y). The multicomponent oxidemay include nitrogen (e.g., Hf_(x)Si_(1-x)O_(2-y)N_(y)) according to anexemplary embodiment. The charge blocking layer having a compositiongradient may be disposed between the charge storage layer and thecontrol dielectric layer, or between the control dielectric layer andthe gate contact of the memory device. According to some exemplaryembodiments, the gate stack may include both a first and a second chargeblocking layer. One or both charge blocking layers may have acomposition gradient, as described herein.

CONCLUSION

While various embodiments of the present invention have been describedabove, it should be understood that they have been presented by way ofexample only, and not limitation. It will be apparent to persons skilledin the relevant art that various changes in form and detail can be madetherein without departing from the spirit and scope of the invention.Thus, the breadth and scope of the present invention should not belimited by any of the above-described exemplary embodiments, but shouldbe defined only in accordance with the following claims and theirequivalents.

1. A gate stack of a memory device, the gate stack comprising: a chargestorage layer comprising localized charge traps on a tunnelingdielectric layer; a first dielectric layer comprising a first oxynitridehaving a first dielectric constant directly on the charge storage layer;a second dielectric layer comprising an oxide having a second dielectricconstant directly on the first dielectric layer; and a third dielectriclayer comprising a second oxynitride having a third dielectric constantdirectly on the second dielectric layer, wherein the first and thirddielectric constants are greater than the second dielectric constant. 2.The gate stack of claim 1, wherein the memory device exhibits a chargeloss of about 5 V or less over a period of 24 hours at a temperature of250° C.
 3. The gate stack of claim 1, wherein the second dielectriclayer has a thickness of from about 8 nm to about 16 nm.
 4. The gatestack of claim 1, wherein each of the first and third dielectric layershas a thickness of from about 1 nm to about 6 nm.
 5. The gate stack ofclaim 1, wherein the first and third dielectric layers comprise at leastone of hafnium oxynitride and silicon oxynitride.
 6. The gate stack ofclaim 1, wherein the second dielectric layer comprises aluminum oxide.7. The gate stack of claim 1, wherein the localized charge traps aremetal nanocrystals.
 8. The gate stack of claim 1, wherein the firstdielectric layer includes a lower concentration of nitrogen than thethird dielectric layer.
 9. The gate stack of claim 1, wherein the memorydevice exhibits a charge retention of about 85% or greater over a periodof 24 hours at a temperature of 250° C.
 10. The gate stack of claim 9,wherein the memory device exhibits a charge retention of about 90% orgreater over the period of 24 hours at the temperature of 250° C.
 11. Agate stack of a memory device, the gate stack comprising: a chargestorage layer comprising polysilicon on a tunneling dielectric layer; afirst dielectric layer comprising a first oxynitride having a firstdielectric constant directly on the charge storage layer; a seconddielectric layer comprising an oxide having a second dielectric constantdirectly on the first dielectric layer; and a third dielectric layercomprising a second oxynitride having a third dielectric constantdirectly on the second dielectric layer, wherein the first and thirddielectric constants are greater than the second dielectric constant,and wherein the memory device exhibits a charge retention of about 85%or greater over a period of 24 hours at a temperature of 250° C.